西安碳素结构钢钢板和宽钢带的牌号和化学成分
碳素结构钢热轧厚钢板和宽钢带的牌号和化学成分
|
牌号 |
钢板材质化学成分(质量分数)(％) |
|
C |
si |
Mn |
P |
S |
Cr |
Ni |
Cu |
|
≤ |
|
05F |
≤O．06 |
≤0.03 |
≤O．40． |
O．035 |
0.040 |
O．10 |
O．25 |
0.25 |
|
08F |
O．05～0.11 |
≤0.03 |
0.25～0.50 |
0.035 |
O．040 |
O．10 |
O．25 |
O.25 |
|
08 |
O．05～O．12 |
O．17～O．37 |
O．35～0.65 |
O．035 |
O．040 |
O．10 |
O，25 |
O．25 |
|
10F |
0.07～O．14 |
≤O．07 |
0.25～0.50 |
O．035 |
O．040 |
O．15 |
O．25 |
0.25 |
|
10 |
O．07～0.14 |
O．17～O．37 |
0.35～O．65 |
O．035 |
0.040 |
O．15 |
O．25 |
O．25 |
|
15F |
0.12～O．19 |
≤O．07 |
O．25～O．50 |
0.035 |
O．040 |
0.25 |
0.25 |
0.25 |
|
15 |
0.12～0.19 |
O．17～O．37 |
0.35～O．65 |
O．035 |
0.040 |
0.25 |
0.25 |
O．25 |
|
20F |
O．17～O．24 |
≤O．07 |
O．25～O．50 |
O．035 |
0.040 |
0.25 |
0.25 |
0.25 |
|
20 |
O．17～O．24 |
O．17～O．37 |
O．35～0.65 |
O．035 |
O．040 |
O．25 |
O．25 |
0.25 |
|
25 |
O．22～O．30 |
0.17～O．37 |
0.50～O．80 |
0.035 |
0.040 |
O．25 |
0.25 |
O．25 |
|
30 |
0.27～O．35 |
O．17～0.37 |
O．50～O．80 |
O．035 |
0.040 |
0.25 |
O．25 |
0.25 |
|
35 |
0.32～O．40 |
O．17～O．37 |
0.50～O．80 |
O．035 |
O．040 |
0.25 |
0.25 |
0.25 |
|
40 |
O．37～0,45 |
0.17～O．37 |
O．50～O．80 |
0.035 |
O．040 |
0.25 |
0.25 |
0.25 |
|
45 |
O．42～O．50 |
0.17～0.37 |
0.50～0.80 |
0.035 |
0.040 |
0.25 |
O．25 |
O．25 |
|
50 |
O．47～O．55 |
0.17～O．37 |
0.50～O．80 |
O．035 |
O．040 |
O．25 |
0.25 |
0.25 |
|
55 |
O．52～O．60 |
O．17～O．37 |
0.50～0.80 |
O，035 |
O．040 |
O．25 |
0.25 |
O．25 |
|
60 |
O．57～O．65 |
O．17～O．37 |
O．50～O．80 |
0.035 |
O．040 |
O．25 |
0.25 |
O．25 |
|
65 |
0.62～O．70 |
0.17～O．37 |
O．50～O．80 |
O．035 |
O．040 |
0.25 |
0.25 |
O．25 |
|
70 |
O．67～0.75 |
0.17～0.37 |
0.50～O．80 |
O．035 |
0.040 |
O．25 |
O．25 |
O．25 |
|
20Mn |
O．17～0.24 |
0.17～0.37 |
O．70～1.00 |
O．035 |
O．040 |
0.25 |
0.25 |
0.25 |
|
25Mn |
0.22～0.30 |
0.17～0.37 |
O．70～1.00 |
0.035 |
0.040 |
O．25 |
O．25 |
0.25 |
|
30Mn |
0.27～0.35 |
O．17～O．37 |
O．70～1.00 |
O．035 |
O．040 |
O．25 |
O．25 |
0.25 |
|
40Mn |
0.37～O．45 |
0.17～O．37 |
0.70～1．00 |
O．035 |
O．040 |
0.25 |
0.25 |
O．25 |
|
50Mn |
O．48～O．56 |
0.17～0.37 |
O．70～1．oo |
O．035 |
0.040 |
O．25 |
0.25 |
O．25 |
|
60Mn |
0.57～O．65 |
O．17～O．37 |
O．70～1.00 |
0.035 |
O．040 |
O．25 |
0.25 |
O．25 |
|
65Mn |
0.62～0.70 |
O．17～0.37 |
O．90～1.20 |
0.035 |
O．040 |
0.25 |
O．25 |
0.25 |
注：1．08钢允许用铝代替硅脱氧。此时，钢中含锰量下限为0．25％，含硅量不大于0．03％，钢中酸溶铝AL含量为0．015％～0．065％或全铝ALt.含量为0．02％～0．07％，牌号为08Al。
2．上述含量皆指质量分数。
(3)交货状态钢板和钢带以热处理(正火、退火或高温回火)状态交货。
|